刘长久,刘勇平,张丽静,卢艳芳,王国强.SDBS掺杂聚苯胺的溶解性和防腐蚀性研究[J].广西科学,2003,10(3):220-222. [点击复制]
- Liu Changjiu,Liu Yongping,Zhang Lijing,Lu Yanfang,Wang Guoqiang.Solubility and Corrosion Protection of SDBS Doped Polyaniline[J].Guangxi Sciences,2003,10(3):220-222. [点击复制]
|
|
| 摘要: |
| 用化学氧化聚合法合成易溶于有机溶剂的十二烷基苯磺酸钠(SDBS)掺杂聚苯胺,研究反应温度对聚苯胺溶解性、SDBS和浓盐酸用量对聚苯胺溶解性和防腐蚀性的影响,并通过塔费尔曲线研究聚苯胺对A3钢防腐蚀性能的影响。结果发现,反应温度为10℃制备的聚苯胺在各有机溶液中的溶解性最大;SDBS与苯胺的质量比为2:1时,合成的聚苯胺具有较大的溶解性和防腐蚀性;浓盐酸用量为10ml时,能够获得有较大溶解性的聚苯胺,浓盐酸用量对聚苯胺的防腐性影响不大;聚苯胺涂层能使钢铁自然腐蚀电位正移150mV,钢铁腐蚀电流密度由10-7A/cm2变到10-8A/cm2,提高了钢铁的防腐蚀性能。 |
| 关键词: 聚苯胺 十二烷基苯磺酸钠 腐蚀性 溶解性 |
| DOI： |
| 投稿时间：2003-03-17修订日期：2003-04-28 |
| 基金项目: |
|
| Solubility and Corrosion Protection of SDBS Doped Polyaniline |
|
Liu Changjiu, Liu Yongping, Zhang Lijing, Lu Yanfang, Wang Guoqiang
|
| (Department of Material and Chemical Engineering, Guilin Institute of Technology, 12 Jianganlu, Guilin, Guangxi, 541004, China) |
| Abstract: |
| The polyaniline (PAn) with high solubility doped with SDBS was synthesized by using chemical oxidation.The effects of polymerization conditions on the solubility of Pan in organic solvents and corrosion protection on 3A steel were studied.The effects of polyaniline on corrosivity of 3A steel are also studied according to the Tafle curve.It showed that the polyaniline synthesized under 10℃ has the strongest solubility in various kinds of organic solution;the polyaniline synthesized when the quality proportion of SDBS and aniline is 2:1 has stronger corrosivity and solubility;and the polyaniline synthesized with 10 ml of dense hydrochloric acid has the stronger solubility,but the quantity of the dense hydrochloric acid has a little effect on the corrosivity of polyaniline.The polyaniline coating may change the corrosion potential of steel from 150 mV to positive direction,and changed the corrosion current density from 10-7 A/cm2 to 10-8 A/cm2.The antiseptic ability of steel has improved by coating with PAn. |
| Key words: polyaniline SDBS corrosion solubility |