| 摘要: |
| 采用正交试验方法研究影响混合碱法制备甘蔗渣基活性炭性能的4种工艺因素:活化剂配比、料液比、活化温度及活化时间。结果表明,影响甘蔗渣活性炭吸附性能的工艺因素的强弱秩序为:活化时间、活化温度、活化剂配比、料液比;样品的亚甲基蓝吸附值随着活化温度的升高或活化时间的延长而呈先增后降的变化规律。其最佳工艺为:活化剂配比(KOH:NaOH)7.4:1、料液比1.18:1、浸渍时间24h、活化温度923K、活化时间0.42h。经优化工艺制得的甘蔗渣基活性炭样品的亚甲基蓝吸附值为12.7ml/0.1g,为活性炭国家标准(GB/T13803.4-1999)中一级品的1.4倍。 |
| 关键词: 甘蔗渣 活性炭 工艺 正交试验 |
| DOI： |
| 投稿时间：2008-11-17 |
| 基金项目:广西教育厅科研项目(200707MS032);广西环境工程与保护评价重点实验室主任基金项目(桂科能0702Z020)资助 |
|
| Studies on the Technology of Bagasse-Based Activated Carbon Prepared by Mixed Base Method |
|
JIANG En-yuan, LIAO Qin-hong, HUANG Ying, LIANG Dong-lian, MENG Mian-wu
|
| (College of Environment and Resources, Guangxi Normal University, Guangxi Key Laboratory of Environmental Engineering, Protection and Assessment, Guilin, Guangxi, 541004, China) |
| Abstract: |
| The influencing factors such as the ratio of activating agents,the ratio of bagasse to mixed base,the activation temperature and time on properties of bagasse-based activated carbon prepared by mixed base method were systematically investigated by means of orthogonal test.The results showed that the sequence in terms of influence degree on the adsorption performance of the samples was as follows:activation time > activation temperature > activating agent > the ratio of bagasse to mixed base.The methylene blue adsorption value of the samples would increase first and then decrease with the prolongation activation time or the increase of activation temperature.The optimum technology on preparing activated carbon was found to be as follows:infusion time of Bagasse in the activating agent 24h,ratio of the activating agents (KOH∶NaOH)7.4∶1,ratio of bagasse to mixed base 1.18∶1,activation temperature 923K and activation time 0.42h.The methylene blue adsorption value of the sample prepared under the optimal conditions was 12.7 ml/0.1g which was 1.4 times as that of activated carbon of the first grade standard in GB/T13803.4-1999. |
| Key words: bagasse activated carbon technology orthogonal test |